Ceresit CM 17 flexible mortar S1 thin-bed mortar
5 |10 | 20 x 25kg flexible tile adhesive
Ceresit CM 17 PRODUCT DESCRIPTION
long open time
high stability
for wall and floor
inside and outside
available after 24 hours
AREAS OF APPLICATION
For preparing and laying ceramic tiles and slabs, fine stoneware and insulation panels.
To ensure a flexible adhesive bed and to avoid Constraining stresses on critical substrates.
On heated screeds, balconies, terraces and facades, especially young ones precast concrete elements
For repair and leveling coats prior to laying in the event of unevenness up to approx. 8 mm.
SURFACE PREPARATION
CM 17 adheres to all solid, load-bearing, clean, dry and damp Substrates that are free from separating substances.
Remove coatings with insufficient load-bearing capacity.
Plasters of mortar groups P II/P III (minimum age 28 days), cement screeds (minimum age 28 days, residual moisture = 2 wt.-%, heated screed = 1.8 wt.-%) and Concrete (minimum age 3 months) can be covered directly with tiles
PROCESSING
Mix CM 17 in clean, clear water until there are no lumps or lumps.
Approx. 9.0–10.5 l of water are required to mix 25 kg of CM 17.
For partial amounts, observe the mixing ratio of 2.3 RT powder to approx. 1 RT water
After a maturing time of approx. 5 minutes, mix the mortar again.
Adjust the necessary consistency carefully with water.
Thin-bed mortar according to the recognized rules of technology in the Process thin-bed process.
Allow for a skin formation time of approx. 30 minutes.
Choose the toothing of the comb spatula so that there is a break-up of at least 65 %
Fresh mortar residues can be cleaned with water, hardened material can only be closed mechanically remove.
Grout after approx. 24 hours.
CONSUMPTION
Basis: synthetic resin-modified cement combination with mineral fillers
(reduced chromate)
thin bed mortar
DIN/EN 12 004, C2 TE
Bulk density: approx. 1.29kg/dm³
Mixing ratio: approx. 9.0 l (stable) to 10.5 l (soil) water for 25 kg
Maturation time: 5 minutes
Processing time: approx. 2 hours
Processing temperature: 5°C – 30°C
Open time: about 30 minutes
Slipping: <0.10mm
Available after: 24 hours
Temperature resistance: -30°C – 70°C
Adhesive tensile strength for all types of storage: > 1.0 N/mm²
Consumption (approx. information):
Shelf life: tightly closed, cool and dry, approx. 6 months, opened container process at short notice
IMPORTANT INSTRUCTIONS
Only process the material when it is dry and at temperatures between +5 °C and +30 °C.
CM 17 contains cement and has an alkaline reaction with water, therefore skin and eyes protection.
In case of contact, rinse thoroughly with water.
In case of contact with eyes consult a doctor.
We particularly refer to DIN 18 332, DIN 18 157, DIN 18 515 and the leaflets of the Central Association of the German Construction Industry.